UHLÍKOVÁ NÁSTROJOVÁ OCEL U7A/U7, C70U, C70W1, C70W2, 1.1520, 1.1620 PODLE PN-H-85020, DIN 17350, ISO 4957.
| Standard | Třída oceli | ||||||
|---|---|---|---|---|---|---|---|
| Chemické složení procent | |||||||
| C: | mn: | To jo: | Q: | S: | Cr: | Ani: | Cu: |
| PN | N7E | ||||||
| 0.65 - 0.74 | 0.15 - 0.30 | 0.15 - 0.30 | <0.025 | <0.025 | <0.15 | <0.20 | <0.20 |
| PN | N7 | ||||||
| 0.65 - 0.74 | 0.15 - 0.35 | 0.15 - 0.35 | <0.030 | <0.030 | <0.20 | <0.25 | <0.25 |
| GOST | U7A - У7А | ||||||
| 0.65 - 0.74 | 0.17 - 0.28 | 0.17 - 0.33 | <0.025 | <0.018 | <0.20 | <0.25 | <0.25 |
| GOST | U7 - У7 | ||||||
| 0.66 - 0.73 | 0.20 - 0.40 | 0.15 - 0.35 | <0.030 | <0.028 | <0.20 | <0.25 | <0.25 |
| ISO | C70W1 - C70U - 1.1520 | ||||||
| 0.65 - 0.75 | 0.10 - 0.40 | 0.10 - 0.30 | <0.030 | <0.030 | - | - | - |
| RÁMUS | C70W2 - 1.1620 | ||||||
| 0.65 - 0.74 | 0.10 - 0.35 | 0.10 - 0.30 | <0.030 | <0.030 | - | - | - |
Specifikace a použití C70U, U7A, C70W1, C70W2 -
Hluboce a povrchově kalená uhlíková ocel s nejnižším obsahem uhlíku z uhlíkových materiálů N12E. Vyznačuje se vysokou odolností proti nárazu, úderům a poměrně vysokou tvrdostí. Pokud mluvíme o jeho nevýhodách, vyznačuje se nízkou odolností proti oděru a nízkou obrobitelností. N7E se používá k výrobě dřevoobráběcích nástrojů, měkkých kamenů, prkének, malých vysekávacích zápustek pro práci za tepla, kovacích kladiv. V některých případech může být použit jako náhrada pružinových ocelí
Mechanické vlastnosti U7A, C70W1, C70W2
Měkký stav - tvrdost<187 HB Estado endurecido - dureza >57HRC
Tepelné zpracování: procesy a teploty:
Měkčí žíhání při 680 - 710 C Reliéfní žíhání při 600 - 700 C Temp Hardden při 780 - 820 C Temp Quench při 170 - 190 C
V uvedených kvalitách firma dodává
Tyče válcované za tepla C70U, C70W1, C70